Water-soluble self acid-doped polyaniline, method of preparation thereof, and polymer blends made therefrom

ABSTRACT

The present invention discloses a water-soluble self-acid-doped polyaniline, and its sodium salt, which can be cast into free-standing films from their aqueous solutions. A process for preparing a water-soluble self-acid-doped polyaniline is also disclosed, which comprises reacting a polyaniline with a strong base to convert the amino nitrogen thereof to anionic nitrogen; reacting sultone with the anionic nitrogen to form a side chain alkanesulfonic acid group; doping with protonic acid to form precipitate; dissolving (undoping) the precipitate in an alkaline aqueous solution; removing excess alkali from the alkaline aqueous solution; and contacting the resulting aqueous solution with a H +  -type ion exchange resin. Moreover, an aqueous solution of the present water-soluble self-acid-doped PAn can be easily mixed with an additional water soluble polymer or polymer emulsion, which can then be cased into a polymer blend film having improved mechanical properties and coupling strength to a substrate.

This application is a division of Application Ser. No 08/501,593 filed Jul. 12, 1995 now U.S. Pat. No. 5,641,859.

BACKGROUND OF THE INVENTION

Polyaniline (PAn) is stable in air and has a relatively low manufacturing cost. In addition, PAn has been found to be very useful in various applications, such as: material for making battery electrodes due to its oxidation-reduction properties, material for making pH sensor due to its proton exchange property, material for making a display element due to its electrochromic property, and electromagnetic interference shielding and antistatic coating. Moreover, in 1990, Bridgestone Co. of Japan U.S. Pat. No. 5,066,556 (1991); U.S. Pat. No. 4,957,833 (1990)! used polyaniline deposited on a current collector as a working electrode in conjuction with a lithium electrode to produce a button battery with a discharge capacity of 80 Ahr/kg. Ricoh Co. of Japan U.S. Pat. No. 4,999,263 (1991); U.S. Pat. No. 4,948,685 (1990)! used a polyaniline membrane of 0.05 mm thick deposited on a porous metallic membrane to produce a film-type battery with outside dimensions of 50 mm long, 50 mm wide and 0.9 mm thick. Sony Co. of Japan (Modern Plastics Int., August (1991) 33) utilized polyaniline as an antistatic layer on a high density magnetic memory disc (4 M).

Polyaniline (PAn) basically has a structure which can be represented by the following formula (Faraday Discuss Chem. Soc., 88 (1989) 317): ##STR1## wherein 0≦y≦1. It is termed leucoemeraldine, emeraldine and pernigraniline, when y is 0, 0.5 and 1, respectively.

A conjugated conducting polymer in general has a conductivity of about 10⁻¹² ˜10⁻¹⁹ S/cm in the undoped state, which is increased to a value of about 10⁰ ˜10⁵ S/cm after the conjugated conducting polymer is oxidativeley doped. Polyaniline (PAn) is different from other conjugated conducting polymers in that it can be doped to become a conducting form without requiring their π-electrons to be changed through protonation by exposure to an appropriate protonic acid in aqueous solution Chiang, J. C.; MacDiarmid, A. G. Synth. Met. 1986, 13, 193-205!. Yue and Epstein have synthesized a protonic acid self-doped PAn by reaction of emeraldine base with fuming sulfuric acid to give a sulfonic acid ring-substituted PAn having a conductivity of 0.1 S/cm; however, it is insoluble in the acid form (doped) and can be made soluble only when it is converted to a salt form (undoped) Yue, J.; Epstein, A. J. J. Am. Chem. Soc. 1990, 112, 2800-2801. Yue, J.; Wang, Z. H.; Cromack, K. R.; Epstein, A. J.; MacDiarmid, A. G. J. Am. Chem. Soc. 1991, 113, 2665-2671!. Genies et al. also have attempted to synthesize a self-doped PAn by reaction of emeraldine base directly with propane or butane sultone Hany, P.; Genies, E. M.; Santier, C. Synth. Met. 1989, 31, 369-378!. However, the reaction product has a very poor solubility and low conductivity (˜10⁻⁹ S/cm). So far, all the self-acid-doped PAns reported in the prior art are insoluble, and thus their applications are limited. Dao and co-workers have synthesized a water soluble polyaniline, poly(aniline-propanesulfonic acid) (PAPSA), by reaction of leucoemeraldine base (a fully reduced PAn) with propanesultone Bergeron, J. Y.; Chevalier, J. W.; Dao, L. H. J. Chem. Soc., Chem. Commun. 1990, 180-182!. However. the PAPSA is supposed to have no imnine nitrogen (--N═) to allow self-acid-doping, although they have claimed the appearance of a strong absorption band at about 900 nm, which always appears for protonic acid-doped PAn. Recently, IBM reported that a water-soluble poly(aniline-co-N-(4-sulfophenyl)aniline) has been synthesized by copolymerization Macromolecules 1994, 27, 3625-3631!. However, this product was found via elemental analysis that it is not self-acid-doped, but is HCI-doped PAn. In addition, this PAn is only soluble in aqueous NH₄ OH solutions, and is not soluble in water.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows IR spectra of polyaniline (curve a) and poly(aniline-co-sodium N-propanesulfonate aniline) (curve b).

FIG. 2 shows UV-vis spectra of poly(aniline-co-sodium N-propanesulfonic acid aniline) in aqueous solution (curve a), as solid film coated on a glass substrate (curve b), and in aqueous solution neutralized with ˜2% NaOH aqueous solution (curve c).

FIG. 3 shows electron spin resonance (ESR) spectra of poly(aniline-co-sodium N-propanesulfonic acid aniline) in the form of aqueous solution (curve a), and as solid film (curve b).

DETAILED DESCRIPTION OF THE INVENTION

Here, we report a successful preparation of a novel water-soluble self-acid-doped polyaniline, and its sodium salt, which can be cast into free-standing films from their aqueous solutions. In one of the preferred embodiments of the present invention, poly(aniline-co-N-propanesulfonic acid-aniline) (PAPSAH) was synthesized and a film formed from its aqueous solution exhibited a conductivity of 3×10⁻² S/cm without external doping. This conductivity is sufficiently high so that the water-soluble self-acid-doped polyaniline disclosed in the present invention can be used as an electromagnetic interference shielding (EMI shielding) (10⁻³ S/cm), electrostatic-discharge (ESD) (10⁻⁵ S/cm) or antistatic (10⁻⁹ S/cm) material. Moreover, an aqueous solution of the water-soluble self-acid-doped PAn of the present invention can be easily mixed with a water soluble polymer or polymer emulsion, which can then be casted into a polymer blend film having improved mechanical properties and adhesion strength to a substrate, and thus facilitating the workability of the water-soluble self-acid-doped PAn of the present invention in various applications.

A preferred process for preparing a water-soluble self-acid-doped polyaniline in accordance with the present invention comprises the following steps:

a) dissolving a polyaniline having formula (A) as follows in an organic solvent: ##STR2## wherein R₁, R₂, R₃, R₄ are independently --H, --CH₃, --C₂ H₅, --C₃ H₇, --OR₇, --SR₇, --F, --Cl, --Br, --I, --COR₇, --NHCOR₇, --NO₂, --COOR₇ or --CN, wherein R₇ is a lower alkyl, aryl or aryl (lower alkyl); 0<y<1; and n is an integer equal to or greater than 2, and preferably less than 5000;

b) adding a strong base, such as NaH and alkali metal hydroxides, preferably NaH, into the resulting organic solution of step a), and said strong base reacting with the polyaniline so that the amino nitrogen of said polyaniline is converted to anionic nitrogen;

c) adding sultone into the resulting reaction mixture of step b) and said sultone reacting with said anionic nitrogen of said polyaniline;

d) adding the resulting reaction mixture of step c) into an aqueous solution containing a protonic acid to form a precipitate;

e) removing said precipitate from the resulting mixture of step d);

f) dissolving said precipitate of step e) in an alkaline aqueous solution;

g) purying the resulting aqueous solution from step f) by subjecting it to a purifying treatment, such as a dialysis treatment with a semipermeable membrane in deionized water, to remove excess alkali in said alkaline aqueous solution;

h) contacting the resulting purified aqueous solution of step g) with a H⁺ -type ion-exchange resin to form an aqueous solution containing a polyaniline having the following formula (I): ##STR3## wherein R₁, R₂, R₃, R₄, y and n are defined in the above formula (A); R₅ and R₆ are independently --H or --R₈ SO₃ H, wherein R₈ is C₃ -C₅ alkylene or --CHR₉ --CR₁₀ ═CR₁₁ --CH₂ --, wherein R₉, R₁₀ and R₁₁ are independently -H or alkyl, wherein at least a fraction of R₅ and R₆ in the repeating units of formula (I) are --R₈ SO₃ H, and said fraction ranges from 10 to 99 mol %. Please note that the formula (I) shown is in the undoped state for simplicity.

Preferably, R₁, R₂, R₃, and R₄ are all hydrogen.

Preferably, y is 0.5.

Preferably, R₈ is C₃ -C₅ alkylene.

Preferably, the fraction of R₅ and R₆ in the repeating units of formula (I) being --R₈ SO₃ H ranges from 90 to 99 mol %.

Prior to contacting the purified aqueous solution with an H⁺ -type ion-exchange resin in step h), the present process may further comprise drying the resulting purified aqueous solution of step g) by evaporation to obtain a solid, and dissolving said solid in deionized water to form an aqueous solution which is then contacted with a H⁺ -type ion-exchange resin.

Preferably, the present process further comprises a step i) evaporating water from said aqueous solution containing said polyaniline of formula (I) of step h) to form a concentrated aqueous solution thereof. Said concentrated aqueous solution of said polyaniline of formula (I) can be casted or coated onto a substrate to form a self-acid-doped polyaniline film of formula (I). Once the polyaniline of formula (I) is casted or coated to form a solid film, it is no longer water soluble. Therefore, the water soluble self-acid-doped polyaniline of formula (I) is preferably stored in the form of an aqueous solution, and most preferably an concentrated aqueous solution.

Said organic solvent used in step a) can be dimethylsulfoxide (DMSO), N-methyl-2-pyrrolidone (NMP) or dimethylformamide (DMF).

Said sultone used in step c) can be ##STR4## wherein Me is methyl and Et is ethyl.

The reaction in step b) and c) can be carried out at a temperature ranging from room temperature to 100°C.

Said protonic acid used in step d) can be HCl, HClO₄, HBF₄ or H₂ SO₀₄.

Said alkaline aqueous solution used in step f) can be an aqueous solution of NaOH, KOH or NH₄ OH.

Said purifying treatment in step g), in addition to dialysis treatment, may include any suitable treatment which can remove excess alkali from the alkaline aqueous solution containing the dissolved precipitate of step f), for example H⁺ -type ion exchange treatment. The excess alkali means the cation of the alkali dissolved in the alkaline aqueous solution which is not attracted by the anionic sulfonic acid group, i.e. the amount of alkali exceeding the stoichmetric amount for undoping the protonic acid doped polyaniline.

The present invention also provides a self-acid-doped polyaniline aqueous solution and a film formed from said aqueous solution, in which said self-acid-doped polyaniline has a structure defined as the above formula (I), in which R₁, R₂, R₃, and R₄ are preferably all hydrogen; y is preferably 0.5; R₈ is preferably C₃ -C₅ alkylene; and the fractions of R₅ and R₆ in the repeating units of formula (I) being --R₈ SO₃ H preferably range from 90 to 99 mol %.

A suitable water soluble polymer or polymer emulsion can be easily mixed with the aqueous solution of the self-acid-doped polyaniline of formula (I) to form a polymer blend, in which the mixing ratio of said suitable water soluble polymer ranges from 5 to 95% based on the total weight of the polymers. Said suitable water soluble polymer is selected from the group consisting of poly(ethylene oxide) (PEO), poly(vinyl methyl ether) (PVME), poly(ethylene imine) (PEI) and its esters, poly(acrylic acid) (PAA) and its esters, polyacrylamide (PAAm), poly(methacrylic acid) (PMAA) and its esters, polymethacrylamide (PMAAm), poly(N,N-dimethylacrylamide), poly(N-isopropylacrylamide) (PIPAAm), poly(N-acrylylglycinamide) (PAG), poly(N-methacrylylglycinamide) (PMAG), acrylic copolymers, poly(vinyl alcohol (PVA), poly(vinyl acetate) (PVAc), poly(vinyl acetate-co-vinyl alcohol) (PVAA), polyvinylpyrrolidone (PVP), poly(styrene sulfonic acid) (PSSA) and its esters, poly(ethylenesulfonic Acid) (PESA) and its esters, poly(phosphoric acid) (PPA) and its salts, poly(silicic acid) (PSiA) and its salts, polyvinylamine (PVAm), poly(2-vinylpyridine) (P2VP) and its salts, poly(4-vinylpyridine) (P4VP) and its salts, poly(vinyl sulfuric acid) (PVSA) and its salts, poly(vinyl alcohol-co-vinyl sulfuric acid and its salts, poly(diallyldimethylammonium chloride), poly(vinylphosphonic acid) and its salts, poly(maleic acid) and its salts, poly(2-methacryloyloxyethane-1-sulfonic acid) and its salts, poly(3-methacryloyloxypropane -1-sulfonic acid) and its salts, poly(4-vinylbenzoic acid) and its salts, poly(4-vinylbenzyltrimethylammonium salts), poly 3-(vinyloxy)propane-1-sulfonic acid! and its salts, poly(4-vinylphenol) and its salts, poly(2-vinylpiperidine) and its salts, poly(4-vinylpiperidine) and its salts, and poly(N-vinylsuccinamidic acid) and its salts.

The self-acid-doped polyaniline of formula (I) and said polymer blend can be in the form of an aqueous solution, a film coated on a substrate or an oriented film, a filament or powder.

The invention will be further illustrated by the following examples which are only meant to illustrate the invention, but not to limit it. In the following examples the polymers of formulas (II) to (V) were synthesized: ##STR5##

EXAMPLE 1

Preparation of emeraldine base form of polyaniline (PAn)

The emeraldine base form of polyaniline (PAn, polymer II) was synthesized by a chemical oxidation method similar to that of MacDiarmid and co-workers Chiang, J. C.; MacDiarmid, A. G. Synth. Met. 1986, 13, 193-205!.

To 200 mL 1M HCl aqueous solution 9.3 mL aniline monomer was added. To another 200 1 M HCl aqueous solution 34.23 g (NH₄)₂ S₂ O₈ oxidant was added. The oxidant solution was added dropwise to the monomer solution in an ice bath while stirring and introducing nitrogen therein. The reaction was carried out for 9 hours, the resulting polyaniline precipitate was separated from the reaction mixture by filtration, and washed with 1M HCl aqueous solution and deionized water until the filtrate became colorless. The washed polyaniline was undoped by introducing into 1M NH₄ OH aqueous solution. The mixture was stirred for 24 hours and the insoluble polyaniline was separated by filtration, and washed with deionized water until the filtrate become neutral. The washed polyaniline was dried under vacuum for 48 hours or more to obtain an undoped polyaniline (PAn) powder of formula (II).

The emeraldine base so obtained has an oxidation level of about 0.5 as determined from its N (is) core level spectrum obtained using X-ray photoelectron spectroscopy (XPS), which can be deconvoluted into two peaks with approximately equal areas, one centered at 398.3±0.1 eV (due to the imine nitrogen) and the other located at 399.4±0.1 eV (due to the amine nitrogen). Gel permeation chromatography (GPC) analysis with N-methyl-2-pyrrolidone (NMP) as eluent exhibits a bimodel molecular weight distribution. For the high-molecular-weight fraction, the weight average molecular weight is about 1×10⁶, and for the low-molecularweight fraction, about 1100, as compared with polystyrene standards.

EXAMPLE 2

Preparation of poly(aniline-co-sodium N-propanesulfonate aniline) (PAPSANa)

The dried PAn (2.26 g) prepared in Example 1was reacted with excess NaH (0.9 g) in dried dimethyl sulfoxide (DMSO) at about 45° C. under a dried nitrogen atmosphere for 6 hours to give a green-black solution, in which the original emeraldine base was probably converted to an emeraldine base without H on nitrogen (anionic nitrogen). The solution was subsequently reacted with excess 1,3-propanesultone (4.57 g) for 20 hours at room temperature to give a blue-black solution. The resulting solution was precipitated with 1M HCl aqueous solution, and the green precipitate (HCl-doped PAPSAH) after filtration was washed by a large amount of acetonitrile and then undoped with a NaOH aqueous solution to yield a blue solution, which was then purified by dialysis with semipermeable membrane (Spectra/P or 3 membrane, molecular weight cutoff, 3500) in deionized (DI) water, which was replaced with fresh DI water frequently for 3 days. The polyaniline-co-sodium N-propanesulfonate aniline) (PAPSANa, polymer III) aqueous solution so obtained was concentrated in a vacuum evaporator at a temperature below 40° C. A PAPSANa film can be obtained by casting from this concentrated solution.

FIG. 1 shows the IR spectra of the PAn (curve a) and PAPSANa (curve b). The IR spectrum of the PAPSANa shows that the ratio of the absorption intensity at 1589 cm⁻¹ (due to the quinoid ring) to that at 1498 cm⁻¹ (due to the benzenoid ring) is the same as the corresponding ratio in the emeraldine base PAn before reacting with propanesultone, indicating an oxidation level of about 0.5. This also indicates that 1,3-propanesultone does not give an oxidation reaction during the synthesis of PAPSANa. The presence of the absorption peaks at 1172 and 1044 cm⁻¹ are characteristic of the asymmetric and symmetric O═S═O stretching vibrations, respectively, and the absorption band at 800-600 cm⁻¹ characteristic of stretching modes of C-S and S-0 groups indicate the existence of SO₃ -groups. The presence of an absorption peak at 829 cm⁻¹ (as in the case of the emeraldine base) characteristic of the C-H out-of-plane bending vibrations of the 1,4-disubstituted benzene ring, together with the absence of a splitting of this peak into the two peaks at 820 and 870 cm⁻¹ (which occurs in the case of sulfonic acid ring-substituted PAn, indicates that no ring substitution occurs in the present PAn derivative. The presence of an absorption peak at 1268 cm⁻¹ characteristic of the C_(aliphatic) -N group, together with the presence of the SO₃ - group as stated above, shows that the alkanesulfonic acid groups are linked on the amine nitrogen.

The ¹ H NMR spectrum of the PAPSANa shows a broad peak around 6.6 ppm, characteristic of the aromatic protons, a peak at 3.6 ppm characteristic of the protons of the methylene of the CH₂ CH₂ CH₂ SO₃ Na group bound to the nitrogen, and peaks at 2.0 and 2.9 ppm characteristic of the protons of the next methylene group and the methylene group bound to the sulfur atom, respectively. These results indicate the presence of alkanesulfonic acid groups in the resulting PAn derivative, which is consistent with the IR results.

EXAMPLE 3

Preparation of poly(aniline-co-N-propanesulfonic acid aniline) (PAPSAH)

The polymer, PAPSANa, prepared in Example 2 was converted to poly(aniline-co-N-propanesulfonic acid aniline) (PAPSAH, polymer IV) by dissolving it in DI water and then exchanging Na⁺ for H⁺ using H⁺ -type ion-exchange resin (IR 120H resin from Rohm and Haas Co., U.S.) to give a PAPSAH aqueous solution green in color. A PAPSAH free-standing film can be obtained by casting from a concentrated PAPSAH aqueous solution: however the film is hard and brittle, since it is in the doped state.

Elemental analysis for PAPSAH gives a SIN atomic ratio of 0.48, which implies that almost each amine nitrogen (about 50% of the total nitrogen) in the polymer is linked with a side chain of alkanesulfonic acid.

The free-standing film of PAPSANa has a conductivity of 1.3×10⁻⁶ S/cm, while the pressed pellet and thin film coated on a glass plate of the PAPSAH have conductivity of 1.5×10⁻² and 3×10⁻² S/cm in vacuum at room temperature, respectively. The conductivity was measure by fourpoint probe method. This PAPSAH is in the doped state, as can be confirmed by the electronic spectra of its aqueous solution and thin solid film coated on a glass plate (FIG. 2, curves a and b), which exhibit a π-π* transition of the benzenoid rings at 330 nm and polaron/bipolaron band transitions at about 400 and 860 nm for the solution and 420 and 910 nm for the film. As the PAPSAH aqueous solution was converted to PAPSANa by neutralization with ˜2% of NaOH (aqueous), the polaron/bipolaron bands disappear and a strong exciton transition of the quinoid rings at 573 nm grows at the same time (FIG. 2, curve c). Furthermore, the electron spin resonance (ESR) measurement on the aqueous solution of PAPSAH (FIG. 3, curve a) gives an asymmetric ESR signal with a g value of 2.0042 and a peak-to-peak line width ΔHpp of 10.8 G, and that on the film of PAPSAH (FIG. 3, curve b) gives a symmetric ESR signal with ΔHpp=0.9 G and a spin density of about 6.2×10¹⁹ spin/g and g=2.002865 (both values being rather close to those of HCl-doped PAn (2.2×10²⁰ spin/g, g=2.002868)). The presence of free spins indicates that polarons exist in the self-doped PAPSAH in both the aqueous solution and solid films. Thus, in the self-doped polymer of the present invention the alkanesulfonic acid bound on the side chain attached to the amine nitrogen protonates ("dopes") the imine nitrogen atom to make the polymer conducting.

EXAMPLE 4

Preparation of poly(aniline-co-N-butanesulfonic acid aniline) (PABSAH)

The procedures used to prepare poly(aniline-co-N-butanesulfonic acid aniline) (PABSAH) are similar to those in Examples 2 and 3. The dried PAn (2.26) was reacted with excess NaH (0.9 g) in 100 mL dried dimethyl sulfoxide (DMSO) at about 45°C. under a dried nitrogen atmosphere for 6 hours. The solution was subsequently reacted with excess 1,4-butanesultone (5.09 g) for 20 hours at room temperature. The resulting solution was precipitated with 1M HCl aqueous solution (500 mL), and the precipitate (HCl-doped PABSAH) after filtration was washed by a large amount of acetonitrile and then undoped with a NaOH aqueous solution, which was then filtered and the resulting filtrate was purified by dialysis with semipermeable membrane in deionized (DI) water, which was replaced with fresh Dl water frequently for 3 days. The polyaniline-co-sodium N-butanesulfonate aniline) (PABSANa) aqueous solution so obtained was concentrated in a vacuum evaporator at a temperature below 40°C. A PABSANa film can be obtained by casting from this concentrated solution.

The polymer, PABSANa, was converted to poly(aniline-co-N-butanesulfonic acid aniline) (PABSAH, polymer V) by dissolving it in DI water and then exchanging Na⁺ for H⁺ using H⁺ -type ion-exchange resin to give a PABSAH aqueous solution. A PABSAH free-standing film can be obtained by casting from a concentrated PABSAH aqueous solution. The free-standing film of PABSAH has a conductivity of 3×10⁻³ S/cm in vacuum at room temperature by four-point probe method.

EXAMPLE 5

Preparation of PVA/PAPSAH polymer blend film

0.025 g/mL polyvinyl alcohol (PVA) aqueous solution was prepared by using a polyvinyl alcohol having a weight average molecular weight of 1.0×10⁵ and a hydrolysis degree of 86-89% which is sold under a code BP-17 from Chang Chun Plastics Co., Ltd., Taiwan. A PAPSAH aqueous solution having a solid content of 0.025 g/mL was prepared by using the PAPSAH aqueous solution prepared in Example 3. Each polymer solution was measured 5 mL which were then well mixed with each other. The mixture was coated on a glass substrate to form a film. The conductivity of the film was measured by four-point method and has a value of 1.3×10⁻³ S/cm.

EXAMPLE 6

Preparation of PEO/PAPSAH polymer blend film

0.0125 g/mL polyethylene oxide (PEO) aqueous solution was prepared by using a polyethylene oxide having a weight average molecular weight of 4.0×10⁶ which is available from Polyscience, Inc., U. S. A. A PAPSAH aqueous solution having a solid content of 0.025 g/mL was prepared by using the PAPSAH aqueous solution prepared in Example 3. Each polymer solution was measured 10 mL which were then well mixed with each other. The mixture was coated on a glass substrate to form a film. The conductivity of the film was measured by four-point method and has a value of 1×10⁻³ S/cm.

EXAMPLE 7

Preparation of PVAc/PAPSAH polymer blend film

A polyvinyl acetate (PVAC) emulsion having a solid content of 0.25 g/mL was prepared by using a polyvinyl acetate having an average particle diameter of 1 μm which is sold under a code PE-160 from Chang Chun Plastics Co., Ltd., Taiwan. A PAPSAH aqueous solution having a solid content of 0.025 g/mL was prepared by using the PAPSAH aqueous solution prepared in Example 3. The former was measured 1 mL and the latter was measured 10 mL, which were then well mixed with each other. The mixture was coated on a glass substrate to form a film. The conductivity of the film was measured by four-point method and has a value of 1.5×10⁻³ S/cm.

Having thus described the present invention, which is now deemed appropriate for Letters Patent is set out in the following appended claims. 

What is claimed is:
 1. A self-acid-doped polyaniline having the following formula: ##STR6## wherein R₁, R₂, R₃, R₄ are independently --H, --CH₃, --C₂ H₅, --C₃ H₇, --OR₇, --SR₇, --F, --Cl, --Br, --l, --COR₇, --NHCOR₇, --NO₂, --COOR₇ or --CN, wherein R₇ is a lower alkyl, aryl or aryl(lower alkyl);< y<1; n is an integer equal to or greater than 2; R₅ and R₆ are independently --H or --R₈ SO₃ H, wherein R₈ is C₃ -C₅ alkylene or --CHR₉ --CR₁₀ ═CR₁₁ --CH₂ --, wherein R₉, R₁₀ and R₁₁ are independently --H or alkyl, wherein at least a fraction of R₅ and R₆ in the repeating units of formula (I) are --R₈ SO₃ H, and said fraction ranges from 10 to 99 mol %.
 2. A self-acid-doped polyaniline in accordance with claim 1, wherein said R₁, R₂, R₃, and R₄ are all hydrogen.
 3. A self-acid-doped polyaniline in accordance with claim 1, wherein said y is 0.5.
 4. A self-acid-doped polyaniline in accordance with claim 1, wherein said R₈ is C₃ -C₅ alkylene.
 5. A self-acid-doped polyaniline in accordance with claim 1, wherein said fraction of R₅ and R₆ in the repeating units of formula (I) being --R₈ SO₃ H ranges from 90 to 99 mol %.
 6. A self-acid-doped polyaniline in accordance with claim 1, which is in the form of an aqueous solution, a film, a filament or powder.
 7. A self-acid-doped polyaniline in accordance with claim 1, which is in the form of an aqueous solution.
 8. A self-acid-doped polyaniline in accordance with claim 1, wherein said self-acid-doped polyaniline aqueous solution further contains 0.1 to 99.9% of a water soluble polymer or polymer emulsion based on the total weight of the polymers.
 9. A self-acid-doped polyaniline in accordance with claim 8, wherein said water soluble polymer or polymer emulsion is selected from the group consisting essentially of poly(ethylene oxide) (PEO), poly(vinyl methyl ether) (PVME), poly(ethylene imine) (PEI) and its esters, poly(acrylic acid) (PAA) and its esters, polyacrylamide (PAAm), poly(methacrylic acid) (PMAA) and its esters, polymethacrylamide (PMAAm), poly(N,N-dimethylacrylamide), poly(N-isopropylacrylamide) (PIPAAm), poly(N-acrylylglycinamide) (PAG), poly(N-methacrylylglycinamide) (PMAG), acrylic copolymers, poly(vinyl alcohol (PVA), poly(vinyl acetate) (PVAc), poly(vinyl acetate-co-vinyl alcohol) (PVAA), polyvinylpyrrolidone (PVP), poly(styrene sulfonic acid) (PSSA) and its esters, poly(ethylenesulfonic Acid) (PESA) and its esters, poly(phosphoric acid) (PPA) and its salts, poly(silicic acid) (PSiA) and its salts, polyvinylamine (PVAm), poly(2-vinylpyridine) (P2VP) and its salts, poly(4-vinylpyridine) (P4VP) and its salts, poly(vinyl sulfuric acid) (PVSA) and its salts, poly(vinyl alcohol-co-vinyl sulfuric acid and its salts, poly(diallyldimethylammonium chloride), poly(vinylphosphonic acid) and its salts, poly(maleic acid) and its salts, poly(2-methacryloyloxyethane-1-sulfonic acid) and its salts, poly(3-methacryloyloxypropane -1-sulfonic acid) and its salts, poly(4-vinylbenzoic acid) and its salts, poly(4-vinylbenzyltrimethylammonium salts), poly 3-(vinyloxy)propane-1-sulfonic acid! and its salts, poly(4-vinylphenol) and its salts, poly(2-vinylpiperidine) and its salts, poly(4-vinylpiperidine) and its salts, and poly(N-vinylsuccinamidic acid) and its salts.
 10. A polymer blend which is formed by the self-acid-doped polyaniline aqueous solution containing 0.1 to 99.9% of a water soluble polymer or polymer emulsion based on the total weight of the polymers in accordance with claim 8 and in the form of an aqueous solution, a film, a filament or powder.
 11. A self-acid-doped polyaniline in accordance with claim 9, wherein said water soluble polymer or polymer emulsion is selected from the group consisting essentially of poly(ethylene oxide) (PEO), poly(vinyl alcohol (PVA), and poly(vinyl acetate) (PVAc). 